1. Characteristics: low density, high hardness
2. Purpose: Production of men's and women's sandals, leather shoes, and high-heeled soles
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability （20 OCthe following） | Package |
SX-P-8559 | Milky white liquid or waxy | 1300～1600 | 1.16～1.18 | 6 months | 18Kg/bucket |
SX-I-9722D | Transparent liquid without foreign matter | 200～400 | 1.18～1.20 | 3 months | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-003 is 280±10g/18Kg, the adding amount of water is 60~130g/18Kg, and the adding amount of hardener SX-E-001 is 500-1500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/93~95 | Sole molding density (g/cm3) | 0.35~0.45 | GB/T6638—86 |
Operating temperature(oC) | 40~45/38~42 | hardness (A type) (C type) | 68~82 80~90 | GB/T3903—4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 4.5~5.5 | GB/T6344 |
rise time (s) | 35~49 | Elongation (%) | 300~420 | GB/T6344 |
free bubble density (g/cm3) | 0.16~0.20 | Tear strength (kn/m) | 20.0~25.0 | GB/T10808 |
Metal mold temperature (oC) | 50~60 | Embrittlement temperature
| -22~-27 | GB/T15256 |
Demold time (min) | 4.0~6.0 | Folding endurance test （Second-rate，23 oC） |
| GB/T3903.1 |
|
| NBS wear resistance (%) (data after pre-skin removal) | ≥20 | JCSS |
·Long-term storage of P-8559 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.
·The density of free foam will vary depending on the season (temperature, humidity).
·The demoulding time will increase as the thickness of the molded product increases.
·The physical property data is obtained by testing a 6mm thick test piece.
·Folding resistance conditions: The bending angle is 90 degrees, the frequency is 230 times/min, and an average of 2 6mm incisions are pre-cut at the bending area.
·The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.