1. Features: soft, low density
2. Purpose: Production of insoles and insoles
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability （20 OCthe following） | Package |
SX-P-8066 | liquid or waxy | 1500～2000 | 1.16～1.18 | 6 months | 18Kg/bucket |
SX-I-6395 | Transparent liquid without foreign matter | 100～300 | 1.18～1.20 | 3 months | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-003 is 250±20g/18Kg, the adding amount of water is 0~60g/18Kg, and the adding amount of hardener SX-E-001 is 0-500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/50~55 | Sole molding density (g/cm3) | 0.40~0.45 | GB/T6638—86 |
Operating temperature(oC) | 40~45/38~42 | hardness(A type) (C type) | 30~35 40~50 | GB/T3903—4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 5.5~6.5 | GB/T6344 |
rise time(s) | 35~47 | Elongation (%) | 450~550 | GB/T6344 |
free bubble density (g/cm3) | 0.14~0.18 | Tear strength (kn/m) | 20~25 | GB/T10808 |
Metal mold temperature (oC) | 50~55 |
|
|
|
Demold time (min) | 5.0~7.0 |
|
|
|
|
|
|
|
|
·The mixing ratio is based on the optimal mixing ratio value, which will vary with the type and amount of pigment additives added.
·Long-term storage of P-5013 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.·The density of free foam will vary depending on the season (temperature, humidity).
·The demoulding time will increase as the thickness of the molded product increases.
·The physical property data is obtained by testing a 6mm thick test piece.
·The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.