1. Characteristics: low hardness, good fluidity, polyether type
2. Purpose: Production of insoles and linings, soft mid-low and soft armrest cushions and other handicrafts
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability （20 OC以下） | Package |
SX-P-3530 | liquid or waxy | 600～800 | 1.16～1.19 | 6个月 | 18Kg/bucket |
SX-I-3522 | Transparent liquid without foreign matter | 200～300 | 1.18～1.20 | 3个月 | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-001 is 260±5g/18Kg, the adding amount of water is 25-40g/18Kg, and the adding amount of hardener SX-E-001 is 0-500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/42~45 | Sole molding density (g/cm3) | 0.30~0.70 | GB/T6638—86 |
Operating temperature(oC) | 35~38/38~42 | hardness (A type) (C type) | 10~25 20~45 | GB/T3903—4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 5.0~6.0 | GB/T6344 |
rise time (s) | 25~35 | Elongation (%) | 350~450 | GB/T6344 |
free bubble density (g/cm3) | 0.15~0.25 | Tear strength(kn/m) | 10~13 | GB/T10808 |
Metal mold temperature (oC) | 45~55 | Embrittlement temperature
| -25~-30 | GB/T15256 |
Demold time (min) | 5.0~7.0 | Folding endurance test （Second-rate，23 oC） |
| GB/T3903.1 |
|
| NBSWear-resistant（%） （Data after pre-epidermal removal） |
| JCSS |
·The mixing ratio is based on the optimal mixing ratio value, which will vary with the type and amount of pigment additives added.
·Long-term storage of P-3530 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.·The density of free foam will vary depending on the season (temperature, humidity).
·The demoulding time will increase as the thickness of the molded product increases.
·The physical property data is obtained by testing a 6mm thick test piece.
·Folding endurance conditions: The bending angle is 90 degrees, the frequency is 230 times/min, and an average of two 6mm incisions are pre-cut at the bending area.
·The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.